ArticleName Investigation of the effect of ammonia additions in cementation on forming the structural areas of a hardened layer and profile of carbon and nitrogen concentration
ArticleAuthor P. I. Malenko, A. V. Krokhalev, K. J. Relmasira, A. Yu. Leonov
ArticleAuthorData

Tula State University (Tula, Russia):

Malenko P. I., Cand. Eng., Associate Prof., Chair of Welding, Casting and Technology of Construction Materials, e-mail: malenko@tsu.tula.ru
Relmasira K. J., Post-Graduate, Chair of Metal Physics and Metal Science
Leonov A. Yu., Post-Graduate, Chair of Welding, Casting and Technology of Construction Materials

 

Volgograd State Technical University (Volgograd, Russia)
Krokhalev A. V., Dr. Eng., Associate Prof., Dean of the Faculty of Contruction Materials Technologies

Abstract

Peculiarities of saturation with carbon and nitrogen during cementation with the addition of ammonia and their impact on the formation of structural zones of the layer are observed in the article. It was established as a result of conducted investigations that addition of ammonia in the hardening furnace leads to increase of nitrogen concentration in the surface layer to 0.2%, while the concentration profile of nitrogen is characterized by a sharp drop. As for the profile of carbon concentration on the surface, its reduction to 0.78% takes place, which leads to decrease of microhardness in the surface layer. Troostite on the tooth working surface lies not in the form of a solid strip, but as separate sections along the grain boundaries. Addition of ammonia in the hardening furnace not only at the last stage, but also at the stage of cementation leads to increase of nitrogen concentration in more deep layers and to smooth varying of thickness of the hardened layer. The total process time is shortened by 4 hours, while the eff ective layer thickness is practically not reduced. Further increase of ammonia consumption in a carburizing furnace and a secondary heating furnace leads to increase of nitrogen capacity in the areas of carburizing and hardening furnaces, as well as to increased nitrogen content in the foil, passing through all zones of the unit. Nitrogen content in this case rises both on the surface and in more deep layers of the components. Consumption of the main part of nitrogen for formation of nitrides of alloying elements leads to nitrogen depletion of solid solution around nitrides and forming of troostite selections. Thus, it is shown that increase of ammonia consumption aimed on rise of nitrogen content in steel at the stage of heating for hardening is restricted due to possible nitrogen supersaturation in the surface layer at a small depth (up to 0.2 mm) with forming of nitrides and troostite at the grain boundaries.

keywords High-temperature nitrocarburizing, saturation with carbon and nitrogen, troostite, nitrides, concentration profile, hardened layer, heavyduty gear
References

1. Lakhtin Yu. M., Arzamacov B. N. Chemical-thermal treatment of metals. Moscow : Metallurgiya, 1985. 256 p.
2. Przhenosil B. Nitrocarburizing. Leningrad : Mashinostroenie, 1969. 212 p.
3. Shapochkin V. I., Semenova L. M., Bakhracheva Yu. S., Gyulikhandanov E. L., Semenov S. V. Effect of nitrogen content on the structure and properties of nitrocarburized steel. Metallovedenie i termicheskaya obrabotka metallov. 2010. No. 9. pp. 12–18.
4. Pegisheva S. A., Relmasira K. J. Investigation of the effect of carbon and nitrogen saturation at the high-temperature nitrocarburizing with phase recrystallization on structure and profile of concentration in metal. Izvestiya VolgGTU. 2012. Vol. 9, Iss 6. pp. 169–172.
5. Shapochkin V. I., Semenova L. M., Bakhracheva Yu. S. Nitrocarburizing in the conditions of periodic change of atmosphere cotent. Materialovedenie. 2010. No. 8. pp. 52–57.
6. Pavlovskiy N. R., Ivanova I. A. High-temperature nitrocarburizing of alloyed steel details and equipment in light industry. Uprochnyayushchie tekhnologii i pokrytiya. 2006. No. 12. pp. 12–16.
7. Aliev A. A., Ampilogov A. Yu., Aliev A. A. Carburizing and nitrocarburizing of automotive parts in fluidized bed. Metallovedenie i termicheskaya obrabotka metallov. 2009. No. 4. pp. 31–33.
8. Serebrovskiy V. V., Blinkov B. S., Sabynin E. A. Effect of nitrocarburizing on the machine detail strength. Regionalnyy vestnik. 2016. No. 2. pp. 35–36.
9. Relmasira K. J., Pegisheva S. A. Increasing of strength of heavy-loaded gears. Urgent issues of modern technics and technology : collection of reports of the VII International scientific conference. Lipetsk : Izdatelskiy tsentr «Gravis», 2012. pp. 102–104.
10. Relmasira K. J. Infl uence of non-isothermal conditions in subcooling on carbon and nitrogen saturation and structure of reinforced nitrocarburized layer. All-Russian scientific and technical conference with international participation for youngsters “Innovations in materials science” : collection of materials. Moscow : LLC «Vash poligraficheskiy partner», 2013. pp. 282.
11. Kukhareva N. G. Babul T., Shipko A. A., Shtolik T. N. Carburizing and nitriding of the steel 20 in fluid bed. Mekhanika mashin, mekhanizmov i materialov. 2013. No. 3(24). pp. 62–68.
12. Semenova L. M., Bakhracheva Yu. S. Redistribution of introduction and substitution elements for carbonitriding of 20CrNi3a steel. Vestnik Volgogradskogo gosudarstvennogo universiteta. Seriya 10: Innovatsionnaya deyatelnost. 2012. Iss. 6. pp. 38–43.
13. Semenova L. M., Bakhracheva Yu. S. The increase of mechanical properties at nitrocarburizing with high nitrogen content. Vestnik Volgogradskogo gosudarstvennogo universiteta. Seriya 10: Innovatsionnaya deyatelnost. 2017. No. 1(24). pp. 35–48.
14. Kolmykov V. I., Kosinov E. A. Influence of nitrocarburizing on wearresistance and impact elasticity of instrumental steels. Sovremennye materialy, tekhnika i tekhnologii. 2017. No. 1(9). pp. 120–127.
15. Kostin N. A., Trusova E. V. Fatigue strength of treatable steel 30KhGT after high- and low-temperature nitrocarburization. Auditorium. 2016. No. 4(12). pp. 42–47.
16. Volodin I. M., Kolmykov V. I., Zhosanov A. A. Development and investigation of high-active saturant environment for steel nitrocarburization at low and high temperatures. Physics and technology of nanomaterials and structures : collection of scientific articles of the second International scientific and practical conference. Kursk : JSC «Universitetskaya kniga», 2015. Vol. 1. pp. 43–48.
17. Bakhracheva Yu. S. A new method of predicting the wear resistance of steel. Vestnik Volgogradskogo gosudarstvennogo universiteta. Seriya 10: Innovatsionnaya deyatelnost. 2014. No. 4. pp. 74–78.
18. Dal′Maz Silva W., Dulcy J., Ghanbaja J., Redjaïmia A., Michel G., Thibault S., Belmonte T. Carbonitriding of low alloy steels: Mechanical and metallurgical responses. Materials Science and Engineering: A. 2017. Vol. 693. pp. 225–232.
19. Semenova L. M., Bakhracheva Yu. S., Semenov S. V. Laws of formation of diffusion layers and solution of the diffusion problem in temperature-cycle carbonitriding of steel. Metal Science and Heat Treatment. 2013. Vol. 55, No. 1–2. pp. 34–37.
20. Winter K.-M. Independently controlled carbon and nitrogen potential: A new approach to carbonitriding process. Journal of Materials Engineering and Performance. 2013. Vol. 22, No. 7. pp. 1945–1956.
21. Shapochkin V. I., Semenova L. M., Bakhracheva Yu. S., Gyulikhandanov E. L., Semenov S. V. Effect of nitrogen content on the structure and properties of nitrocarburized steel. Metal Science and Heat Treatment. 2011. Vol. 52, No. 9–10. pp. 413–419.
22. Semenova L. M., Bakhracheva Yu. S. Mechanical properties and phase composition of steel after thermal-cyclic nitrocarburization. Vnedrenie sovremennykh konstruktsiy i peredovykh tekhnologiy v putevoe khozyaystvo. 2013. Vol. 6, No. 6(6). pp. 182–189.
23. Gerasimov S. A., Kuksenova L. I., Lapteva V. G., Fakhurtdinov R. S., Danilov V. D., Smirnov A. E., Gromov V. I., Alekseeva M. S., Shcherbakov Yu. I., Khrennikova I. A. Infl uence of the Activation of the Nicarbing Process on Mechanical Properties of Heat-Resistant Steel. Journal of Machinery Manufacture and Reliability. 2015. Vol. 44, No. 1. pp. 64–69.
24. Grigorchik A. N., Kukareko V. A., Belotserkovskiy M. A., Popok N. N., Sachivko Ya. S. Influence of chemical and heat treatment on the structure and wear-resistant of hypersonic gazotermal coating from steel Sv-08G2S. Aktualnye voprosy mashinovedeniya. 2015. Vol. 4. pp. 370–374.
25. Doshchechkina I. V., Dyachenko S. C., Kostik V. O. Durability increase of tractor gear-shafts. Vestnik Kharkovskogo natsionalnogo avtomobilno-dorozhnogo universiteta. 2006. No. 33. pp. 37–40.
26. Tikhonov A. K., Sardaev N. I., Lazutov P. N. Carbonitriding and Case Hardening of Automotive Parts at OAO “AVTOVAZ”. Metallurgiya mashinostroeniya. 2011. No. 4. pp. 41–42.
27. Kostin N. A. Raising the operating properties of die steel 5Kh2GF by creating carbonitride layers by thermochemical treatment. Metal Science and Heat Treatment. 2016. Vol. 58, No. 7–8. pp. 466–469.
28. Gong M. F., Chen J., Jiang Q. G., Wu S. H. Influence of carbonitriding on microstructure, residual stress and mechanical properties of graded cemented carbides. Journal of Ceramic Processing Research. 2016. Vol. 17, No. 3. pp. 257–264.

Language of full-text russian
Full content Buy
Back