ArticleName Influence of technological parameters of rolling in universal stands on the process of metal displacement from the edges to the longitudinal axis of the roll. Part 1. Technological parameters
ArticleAuthor A. V. Polyakov, R. Shatshu Netshunzim, I. P. Mazur
ArticleAuthorData

Lipetsk State Technical University (Lipetsk, Russia):

A. V. Polyakov, Post-graduate Student, e-mail: Pool_Akov@mail.ru
R. Shatshu Netshunzim, Post-graduate Student;
I. P. Mazur, Dr. Eng., Prof., Head of Metal Forming Dept., e-mail: mazur@stu.lipetsk.ru

Abstract

Edge defects, formed on the continuously cast slab before entering the hot rolling mill, in the wide-strip mill roughing group move from the lateral faces and ribs of the slab to the upper and lower surfaces of the strip plate. This process is facilitated by alternating reduction in vertical and horizontal rolls. The process and reasons for the transition of metal from the ribs and lateral faces of the slab, as well as the defects located on them, to the upper and lower surfaces of the rolled stock during rolling in universal stands of the roughing group of the continuous wide-strip hot rolling mill have been considered. The amount of movement of defects on the horizontal surfaces of the rolled stock directly affects the amount of side trim, which is necessary to ensure the removal of edge defects in subsequent production areas. A mathematical model of slab reduction based on the finite element method using the SIMULIA ABAQUS software package is presented. The mathematical model includes the reduction of the continuously cast slab in three freestanding stands, consisting of vertical and horizontal rolls. The influence of a number of technological parameters and modes of adjustment of the vertical rolls operation, such as the magnitude and distribution of lateral reduction, speed mode, on the amount of metal displacement to the longitudinal axis of the roll has been investigated.

keywords Hot rolling, roughing stands, reduction of slabs, edge defects, rolled crack, mathematical modeling, finite element method
References

1. Brandner М., Elizondo L., Trickl Th., Paar А., Hardt S. Optimization of rolls for hot rolling mills providing better efficiency. Chernye Metally. 2017. No. 7. pp. 24–30.
2. Ogarkov N. N., Platov S. I., Urtsev V. N., Sufyanov D. V., Shemetova Е. S. Study of the displacement of scale fragments during deformation of protrusions and hollows with formation of a defect “rolled scale” and without it. Proizvodstvo prokata. 2018. No. 3. pp. 15–21.
3. Xianghua L., Hailiang Y., Changsheng L. Behaviour of corner surface cracks in V-H rolling process of steel slabs. Paper presented at the 9th International Steel Rolling Conference, CNIT Paris-La Defense, June 19–21, 2006.
4. Shabalov I. P. Industrial study of the transition of metal from the lateral faces of the slab to the main surfaces of the sheet. Proizvodstvo prokata. 2004. No. 9. pp. 3–12.
5. Safyan М. М., Cherner М. I. On the application of the transverse rolling scheme of thick sheets: in the book: Metal Forming. Moscow: Metallurgiya. 1970. pp. 28–35.
6. Mazur I. P. Issues of surface quality control in the production of sheet metal. Stal. 2011. No. 4. p. 31.
7. Mazur I., Koinov T. Quality control system for a hot-rolled metal surface. Frattura ed Integrita Strutturale. 2016. Vol. 10, Iss. 37. pp. 287–296.
8. Medvedev G. А., Lebedev S. А., Shmurygin V. I. Determination of rolling and adjustment parameters of vertical rolls for contiunuous wide-strip hot rolling mill. Works of the First Congress of Rollermen. Moscow: Chermetinformatsiya, 1996. pp. 113–116.
9. Salganik V. М., Pesin А. М., Pustovoytov D. О., Chikishev D. N., Denisov S. V. Development of the efficient scheme for rough rolling of low-alloy steels. Stal. 2008. No. 9. pp. 50–53.
10. Pimenov V. А., Kopylov А. F., Glebov V. P. Influence of the shape of the narrow faces of slabs and their deformation during hot rolling on the topography of surface defects in finished rolled products. Metallurg. 2014. No. 9. pp. 77–79.
11. Pimenov V. А., Shamarin А. V., Polyakov А. V., Mazur I. P. Contouring of vertical rolls in the stand No. 1 of the 2000 hot rolling mill at Novolipetsk steel works in order to reduce the “deformed crack” edged defect. Chernye Metally. 2018. No. 11. pp. 17–21.
12. Lui X., Yu H., Li C., Zhao H. Behaviour of corner surface cracks in V-H rolling process of steel slabs. The 9th International Steel Rolling Conference, CNIT Paris-La Defense, June 19–21. 2006. p. 204.
13. Mazur I. P., Polyakov А. V. Study of the process of metal transition from the lateral faces of the slab to the upper and lower surfaces of the rolled stock during rolling in universal stands in the ABAQUS software package. Vestnik LGTU. 2018. No. 4. pp. 62–71.
14. Rumyantsev M. I., Tulupov O. N. Further developments in simulation of metal forming processes. CIS Iron and Steel Review. 2018. Vol. 16. pp. 21–24.
15. Chun M., Kwon H., Park H. A numerical study of rolled-in scale in the Hot Strip Mill. 9th International Steel Rolling Conference, CNIT Paris-La Defense, June 19–21. 2006.
16. Konovalov Yu. V., Ostapenko А. L., Ponomarev V. I. Calculation of sheet rolling parameters: handbook. Moscow: Metallurgiya, 1986. 429 p.

Language of full-text russian
Full content Buy
Back