ArticleName Production of metallic nickel particles of a given size from nickel (II) salts using sodium borohydride
DOI 10.17580/tsm.2021.07.03
ArticleAuthor Magzhanov R. Kh., Yarovaya O. V., Bondareva G. M.
ArticleAuthorData

D. Mendeleev University of Chemical Technology of Russia, Moscow, Russia:

R. Kh. Magzhanov, Postgraduate Student at the Department of Colloid Chemistry, e-mail: ruh7899@gmail.com
O. V. Yarovaya, Associate Professor at the Department of Colloid Chemistry, Сandidate of Technical Sciences
G. M. Bondareva, Associate Professor at the Department of Physical Chemistry, Сandidate of Technical Sciences

Abstract

Fine nickel particles offer an innovative material which can be used, in particular, as a filler in conducting compositions. However, for successful practical application in the above area the size of such particles should not exceed 12 μm. The method of chemical reduction of salts in liquid phase was selected to produce metallic nickel particles with controlled size. Nickel chloride was used as a salt, and sodium borohydride with its high reduction activity – as a reducing agent. The synthesis was carried out in aqueous medium at room temperature with the [BH4]/[Ni2+] ratio equal to 3.5 mol/mol. The authors looked at the hydrolysis of sodium borohydride in solutions with varying concentrations of alkali and thus determined what concentration of sodium hydroxide would be optimum to stabilize the sodium borohydride solution. Kinetic dependencies of pH and the optical density of the reaction mixture were obtained. Their comparison and analysis helped time-space the processes of nucleation and synthesis suggesting that that was an autocatalytic reaction. The obtained results helped establish that the optimum range of nickel chloride concentrations is 15 to 20 mmol/L. An optical microscope was used to obtain microphotographs of the synthesized particles and determine their sizes as a function of the concentration of the initial salt and the storage time. It was established that the maximum size of the obtained particles in the nickel chloride concentration range of 5 to 20 mmol/L after a week after synthesis was 10 μm. At the same time, when the nickel chloride concentration is 15 to 20 mmol/L, the most probable size of the particles after a week after synthesis is 4–6 μm.
This research was funded by the D. Mendeleev University of Chemical Technology of Russia. Project number: G-2020-019.

keywords Nickel, conducting compositions, chemical reduction, sodium borohydride, fine particles, kinetic dependencies, controlled size
References

1. Surovaya B. E., Bugerko L. N., Surovoy E. P., Bin S. V. Examining nickel nanofilms with the help of the Sauerbrey method. Polzunovskiy vestnik. 2015. Vol. 2, No. 4. pp. 90–94.

2. Karepina E. E., Kurovskiy A. V. Effect of ultrasonic machining on the solubility of nickel nanoparticles in water suspension. 13th International Conference among Undergraduate and Postgraduate Students and Young Researchers “Prospective Development of Basic Sciences”. 2016. Vol. 2, No. 5. pp. 202–204.
3. Logutenko O. A., Titkov A. I., Vorobiev A. M., Yukhin Yu. M., Lyakhov N. Z. Obtaining nanoparticles of nickel by reducing nickel formate in ethylene glycol. Khimiya v interesakh ustoychivogo razvitiya. 2016. Vol. 24, No. 5. pp. 619–626.
4. Hui-Wang Cui, Qiong Fan, Dong-Sheng Li, Xin Tang. Formulation and characterization of electrically conductive adhesives for electronic packaging. The Journal of Adhesion. 2013. Vol. 89. pp. 19–36.
5. Jie Luo, Zhijie Cheng, Chaowei Li, Liangjie Wang et al. Electrically conductive adhesives based on thermoplastic polyurethane filled with silver flakes and carbon nanotubes. Composites Science and Technology. 2016. Vol. 129. pp. 191–197.
6. Wenjuan Cui, Wensheng Lu, Yakun Zhang, Guanhua Lin et al. Gold nanoparticle ink suitable for electric-conductive pattern fabrication using inink-jet printing technology. Colloids and Surfaces A: Physicochemical and Engineering Aspects. 2010. Vol. 358. pp. 35–41.
7. Isaev A. Yu., Petrova A. P., Lukina N. F., Kotova E. V. et al. Conductive adhesives with various fillers. National Russian Science and Technology Conference “Basic and Applied Research in the Area of Developing Adhesives, Binders and Prepregs”. 2018. pp. 14–29.
8. Jun Jie Jing, Jimin Xie, Gao Yuan Chen, Wen Hua Li, Ming Mei Zhang. Preparation of nickel – silver core – shell nanoparticles by liquid-phase reduction for use in conductive paste. Journal of Experimental Nanoscience. 2015. Vol. 10, No. 17. pp. 1347–1356.
9. Dong-Wook Kim, Tae-Hee Kim, Dong-Wha Park. Preparation of silver coated nickel particles by thermal plasma with pre-treatment using ball milling. Advanced Powder Technology. 2018. Vol. 29, Iss. 1. pp. 2686–2692.
10. GOST 9722–97. Nickel powder. Specifications. Introduced: 01.01.1998.
11. Bönnemann H., Richards R. M. Nanoscopic Metal Particles – Synthetic Methods and Potential Applications. European Journal Inorganic of Chemistry. 2001. Vol. 10. pp. 2455–2480.
12. Pugachev V. M., Zakharov Yu. A., Vasilieva O. V., Karpushkina Yu. V., Dodonov V. G. Obtaining and oxidizing nanocrystalline nickel-copper powders. Khimiya v interesakh ustoychivogo razvitiya. 2015. Vol. 23, No. 2. pp. 169–175.
13. Ankur Pandey, Ramachandran Manivannan. A study on synthesis of nickel nanoparticles using chemical reduction technique. Recent Patents on Nanomedicine. 2015. Vol. 5, Iss. 1. pp. 33–37.
14. Raj K. J. A., Viswanathan B. Synthesis of nickel nanoparticles with FCC and HCP crystal structures. Indian Journal of Chemistry. 2011. Vol. 50A, Iss. 2. pp. 176–179.
15. Nichugovskiy G. F. Determining the moisture content of chemical substances. Leningrad : Khimiya, 1977. 198 p.
16. Maltseva N. N., Khain V. S. Sodium borohydride. Moscow : Nauka, 1985. 207 p.
17. Glavee G. N., Klabunde K. J., Sorensen C. M., Hadjipanayis G. C. Borohydride reduction of nickel and copper ions in aqueous and nonaqueous media. Controllable chemistry leading to nanoscale metal and metal boride particles. Langmuir. 1994. Vol. 10. pp. 4726–4730.
18. Watzky M. A., Finke R. G. Transition metal nanocluster formation kinetic and mechanistic studies. A new mechanism when hydrogen is the reductant: slow, continuous nucleation and fast autocatalytic surface growth. Journal of the American Chemical Society. 1997. Vol. 119, No. 43. pp. 10382–10400.
19. Gavrilova N. N., Nazarov V. V., Yarovaya O. V. Microscopy techniques for determining the particle size in disperse materials: Learner’s guide. Moscow : RKhTU im. D. I. Mendeleeva. 2012. 52 p.

Language of full-text russian
Full content Buy
Back