Название Experimental investigations of the nickel alloy laser melting parameters influence on porosity and surface roughness of the complex geometry products during the process of their three-dimensional formation
DOI 10.17580/nfm.2016.12.06
Автор Dub A. V., Beregovskiy V. V., Tretyakov E. V., Shchurenkova S. A.
Информация об авторе

JSC “Science and Innovations”, Moscow, Russia:

A. V. Dub, Professor, First Deputy Director General


Joint Stock Company “Research and Manufacturing Association “Central Research and Development Institute for Mechanical Engineering Technology”, Moscow, Russia:
V. V. Beregovskiy, Deputy Director General, Director of the Institute for Surface and Nanomaterials Technology (ISNT)
E. V. Tretyakov, Deputy Director of the ISNT for production planning work
S. A. Shchurenkova, Head of the Vacuum Coatings and Evacuating Equipment Laboratory, e-mail: svetastch@yandex.ru

Реферат

Presented in the paper are the experimental investigations of the physical parameters (laser output power within the limits of 245-305 W, scanning speed within the limits of 605–1005 mm/s) of selective laser melting of a KhN45MVTUBR (ХН45МВТЮБР) EP-718 (ЭП-718) nickel alloy in the process of a layer-by-layer synthesis of the complex-geometry products with curved elements and honeycomb structures influence on surface roughness, dimensions and density of pores distribution in a grown layer. It is found that the porosity of the complex-geometry samples being studied in the sections parallel and perpendicular to the direction of formation, amounts to 0.58–3.18% depending on the energy density of laser irradiation value, laying within the limits of 244–504 J/m, and the surface roughness varies within the Ra 8.6–19.3 m limits as well. It is determined that surface roughness depends on the energy density of laser irradiation in the same manner as a porosity does as well as pores distribution by their size for different process modes of operation. It is defined that process modes of operation based on high speeds (up to 1005 mm/s) with the linear energy density of laser irradiation of 244–303 J/m cause formation of a great number of coarse pores which appear due to instability of a molten track at high scanning speeds. The process modes of operations based on scanning speed within the 605 mm/s limits leads to increase of the small pores (up to 10 μm) quantity as the linear energy density grows up to 405–504 J/m. It is established that the optimal process mode of operations of a KhN45MVTUBR (EP-718) alloy selective laser melting (SLM) for the complex geometry parts comprises the following parameters: laser output power of 275 W, scanning speed of 605 mm/s, hatching range of 120 μm, laser spot diameter of 80 μm, powder layer thickness of 50 μm, checkerboard scanning strategy.

The work was performed with financial support of the Ministry of Education and Science of the Russian Federation (the unique identifier of the applied scientific research is RFMEFI57915X0125).

Ключевые слова Selective laser melting, nickel alloy, porosity, complex geometry, three-dimensional prototyping
Библиографический список

1. Beregovskiy V. V., Tretyakov E. V., Shchurenkova S. A. Oborudovanie dlya posloynogo izgotovleniya slozhnoprofilnykh izdeliy metodom selektivnogo lazernogo plavleniya MeltMaster3D 550 (Equipment for layer-by-layer manufacturing the profilecomposite articles by the MeltMaster3D 550 selective laser melting method). Materialy II mezhdu narodnoy konferentsii “Additivnye tekhnologii: nastoya shcheye i budushcheye” (Materials of II International conference “Additive technologies: the present and the future”). Moscow, 2016.
2. Carter L. N., Martin C., Withers P. J., Attallah M. M. The influence of the laser scan strategy on grain structure and cracking behaviour in SLM powder-bed fabricated nickel superalloy. Journal of Alloys and Compounds. 2014. Vol. 615. pp. 338–347.
3. Yadroitsev I., Gusarov A., Yadroitsava I., Smurov I. Single track formation in selective laser melting of metal powders. Journal of Materials Processing Technology. 2010. Vol. 210. pp. 1624–1631.
4. Yadroitsev I., Bertrand Ph., Smurov I. Parametric analysis of the selective laser melting process. Applied Surface Science. 2007. Vol. 253. pp. 8064–8069.
5. Gusarov A. V., Yadroitsev I., Bertrand P., Smurov I. Heat transfer modelling and stability analysis of selective laser melting. Applied Surface Science. 2007. Vol. 254. pp. 975–979.
6. Chandrasekhar S. Hydrodynamic and Hydromagnetic Stability. New York : Dover Publications, 1981. 652 p.
7. Xin Zhou, Dianzheng Wang, Xihe Liu, Dan Dan Zhang, Shilian Qu, Jing Ma, Gary London, Zhijian Shen, Wei Liu. 3D-imaging of selective laser melting defects in a Co – Cr – Mo alloy by synchrotron radiation micro-CT. Acta Materialia. 2015. Vol. 98. pp. 1–16.
8. Jianyin Chen, Lijue Xue. Process-induced microstructural characteristics of laser consolidated IN-738 superalloy. Materials Science and Engineering A. 2010. Vol. 527. pp. 7318–7328.
9. Kim I. S., Choi B. G., Hong H. U., Yoo Y. S., Jo C. Y. Anomalous deformation behavior and twin formation of Ni-base superalloys at the intermediate temperatures. Materials Science and Engineering A. Vol. 528. 2011. pp. 7149–7155.
10. Qingbo Jia, Dongdong Gu. Selective laser melting additive manufacturing of Inconel 718 superalloy parts: Densification, microstructure and properties. Journal of Alloys and Compounds. 2014. Vol. 585. pp. 713–721.
11. Investigations on the microstructure and crack formation of IN738LC samples processed by selective laser melting using Gaussian and doughnut profiles. Materials and Design. 2016. Vol. 89. pp. 770–784.
12. SLM Metal Powder. Discover the variety. SLMSolutions. [Electronic resource] : http://slm-solutions.com/sites/default/files/attachment/page/2016/01/151023_slm_metal_powder.pdf

Полный текст статьи Experimental investigations of the nickel alloy laser melting parameters influence on porosity and surface roughness of the complex geometry products during the process of their three-dimensional formation
Назад