Автор | T. Hickel, F. Roters, D. Raabe, J. Neugebauer |
Информация об авторе | Max Plank Institute of Iron Research (Düsseldorf, Germany): Hickel T., e-mail: t.hickel@mpie.de Roters F. Raabe D. Neugebauer J. |
Реферат | Non-empiric methods based on multi-scale simulation allow to predict the main deformation mechanisms in complicated materials depending on alloy composition and technological parameters. Productivity of the new methods is displayed for obtaining of highmanganese steels with tensile strength about 1 GPa and elongation up to 70%. Thereby it can be determined that 20% Mn content leads to especial low value of energy of packing defects (SFE) and to high strength of material. It can also explain why various experimental investigations had very different conclusions about carbon effect on SFE: if TWIP steel is subjected to deformation at room temperature, carbon atoms don’t move practically and leave just near packing defect. However, during heat treatment they move from energy unprofitable positions in the area of packing defect and thereby vary SPE value. |
Ключевые слова | Non-empiric methods, simulation, solidification, packing defect, energy, TWIP steels, manganese |
Библиографический список | 1. Raabe, D.; Roters, F.; Neugebauer, J.; Gutierrez-Urrutia, I.; Hickel, T.; Bleck, W.; Schneider, J. M.; Wittig, J. E.; Mayer, J.: MRS Bulletin 41 (2016), S. 320/25. |
Language of full-text | русский |
Полный текст статьи | Получить |