ArticleName Non-metallic inclusions and hook cracks of high-frequency induction welded pipes
DOI 10.17580/cisisr.2022.02.08
ArticleAuthor A. A. Kazakov, D. V. Kiselev, V. A. Murysev, I. V. Rybalchenko
ArticleAuthorData

Thixomet Ltd. (St. Petersburg, Russia):

A. A. Kazakov, Dr. Eng., Prof., Head of “Metallurgical Examination” Lab., e-mail: kazakov@thixomet.ru
D. V. Kiselev, Technical Director

 

Vyksa Steel Works JSC (Vyksa, Russia):
V. A. Murysev, Chief Specialist, Engineering and Technology Center
I. V. Rybalchenko, Head of the Lab. of Metal Science and Heat Treatment of Metals, Central Plant Laboratory

Abstract

Based on the analysis of foreign experience, it is shown that hook cracks are the most common defect of pipe joints obtained by high-frequency induction welding (HFIW). Particular attention is paid to the non-metallic inclusions (NMIs) that caused this defect. Their composition, origin and ways of elimination are considered. It was found that in the foreign literature the nature of certain oxides found in the vicinity of defects is often declared without objective evidence of their origin. The interpretation technique of NMIs composition, which caused the formation of defects of pipe joints obtained by HFIW, is presented. This technique is a part of the "Metal products quality system", implemented on the basis of Thixomet image analyzer, working in the laboratories of Vyksa Steel Works JSC. The compositions of NMIs found in the discontinuities of welded joint defects of 09G2S steel grade were interpreted using thermodynamic simulation of primary NMIs and generalized for two sets of 65 and 70 defects in each set. These compositions differ significantly from each other and correspond to the following indigenous inclusions: Al2O3, MgO·Al2O3, calcium aluminates, CaO and CaS. The same compounds can form exo-indigenous NMIs conglomerates after the interaction between liquid calcium aluminates and refractories based on MgO or ZrO2, and/or mould powder. The unique ranges of concentration changes of the main elements included in individual phases and their combinations in NMIs conglomerates are used for automated determination of their origin when conducting metallographic examination of defects using the Thixomet image analyzer. Examples of using the origin of NMIs to find the exact place in the secondary steelmaking and steel casting technologies for their improvement and on this basis to improve the quality of HFIW pipe joints are also presented.

keywords Pipes, welding, high frequency induction welding, defects, hook cracks, non-metallic inclusions, thermodynamic simulation, indigenous, exogenous, interpretation
References

1. Technician ERW Weld Discontinuity Characterization Guide. For the API Long Seam Pipeline (LSP) exam. URL: https://www.api.org/-/media/Files/Certification/ICP/ICP-Certification-Programs/UT%20Programs/LSP/Technician%20Characterization%20Guide%20 for%20API%20LSP%20Exam.pdf?la=en&hash=6A3CA97BDDCE851B0CBBAC81ACCD55311BFC7E21 (access date 06.07.2022).
2. API Bulletin on Imperfection Technology, API Bul. 5T1 (R2017), 2017. 65 p. URL: https://standards.globalspec.com/std/10185662/api-bull-5t1 (access date 06.07.2022).
3. Fazzini P. G., Cisilino A. P., Otegui J. L. Experimental validation of the influence of lamination defects in electrical resistance seam welded pipelines. International Journal of Pressure Vessels and Piping. 2005. Vol. 82. pp. 896–904.
4. Joo M. S., Noh K. M., Kim W. K. et al. A Study of Metallurgical Factors for Defect Formation in Electric Resistance Welded API Steel Pipes. Metallurgical and Materials Transactions. 2015. E 2. pp. 119–130. DOI: 10.1007/s40553-015-0049-6 (access date 06.07.2022).
5. Tiratsoo J. Managing pipeline threats. Editor QR 11-9. Hook cracking. URL: https://pipeline-threats.com/plthreats/qr-11-9-hook-cracking/ (access date 06.07.2022).
6. Sima A. Y., Hossein E., Mehrdad F. Hook crack in electric resistance welding line pipe steel. Australian Institute for Innovative Materials - Papers. 2003. 1409. URL: https://ro.uow.edu.au/aiimpapers/1409.
7. Ghosh A. Secondary Steelmaking – principles and applications. CRC Press. 2000. 344 p.
8. Kyada T., Raghu Shant J., Goyal D. et al. Analysis of Micro Cracks Near Weld Line in ERW Pipe of API 5L X70M Grade. Journal of Failure Analysis and Prevention. 2015. Vol. 15. pp. 344–350. DOI: 10.1007/s11668-015-9950-7.
9. Shin M. H., Han J. M., Lee Y. S., Kang H. W. Study on Defect Formation Mechanisms in ERW for API Steel. Proceedings of Biennale International Pipeline Conference IPC. 2014. Vol. 3. 5 p. DOI: 10.1115/IPC2014-33082.
10. Eaves G. N., Cameron S. R., Casey V. J., Nestico P., Bernert W. Hook Crack reduction in ERW line pipe steel. Steelmaking Conference proceedings. 1992. pp. 521–528.
11. Tsai H. Thomas. Characterization of Hook Cracks in Tubular Products and Countermeasures 2007. China Iron and Steel – 2007.
12. Sofras Ch., Bouzouni M., Voudouris N., Papaefthymiou S. Investigation of penetrator defect formation during high frequency induction welding in pipeline steels. MATEC Web of Conf. ICEAFVI. 2021. Vol. 349. DOI: 10.1051/matecconf /202134904002.
13. Okabe T., Toyoda S., Goto S., Kato Y., Yasuda K., Nakata K. Numerical Analysis of Welding Phenomena in High-Frequency Electric Resistance Welding. KEM. 2014. Vol. 622–623. pp. 525–531. DOI: 10.4028/www.scientific.net/kem.622-623.525.
14. Kaba M., Altay M., Çimenoglu H. An Investigation on the Longitudinal Cracking of Electric Resistance Welded Steel Pipes. Journal of Failure Analysis and Prevention. 2020. Vol. 20. pp. 657–662. DOI: 10.1007/s11668-020-00880-3.
15. Kim C. M., Kim J. K. The effect of heat input on the defect phases in high frequency electric resistance welding. Metals and Materials International. 2009. Vol. 15. pp. 141–148. DOI: 10.1007/s12540-009-0141-5.
16. GOST 31447–2012. Steel welded pipes for main gas, oil and oil products pipelines. Introduced: 01.01.2015.
17. GOST 59496–2021. Steel welded pipes. Defects of welded joints. Terms and definitions. Introduced: 01.06.2021.
18. Adaba O. et al. An SEM/EDS Statistical Study of the Effect of Mini-Mill Practices on the Inclusion Population in Liquid Steel. Proceedings of the 9th International Conference and Exhibition on Clean Steel. 2015, Budapest, Hungary. 2015. September.
19. Kazakov А. А., Murysev V. А., Kiselev D. V. Interpretation of nature of non-metallic inclusions in assessing the quality of metal products in the industrial conditions. Chernye metally. 2021. No. 9. pp. 47–54.
20. Kazakov A. A., Murysev V. A., Kiselev D. V. Non-metallic inclusions interpretation technique for factory expertise of metal product defects. CIS Iron and Steel Review. 2021. Vol. 22. pp. 41–49. DOI: 10.17580/cisisr.2021.02.08.
21. K.C. Ahlborg. Fifth International Conference on Clean Steel, OMBKE, Budapest, Hungary. 1997. pp. 151–156.
22. Li Y., Yang W., Zhang L. Formation mechanism of MgO containing inclusions in the molten steel refined in MgO refractory crucibles. Metals. 2020. Vol. 10. 444 p. DOI: 10.3390/met10040444.
23. Liu Ch., Gao Xu, Kim S.-J., Ueda Sh., Kitamura Sh. Dissolution behavior of Mg from MgO–C refractory in Al-killed molten steel. ISIJ International. 2018. Vol. 58. Iss. 3. pp. 488–495. DOI: 10.2355/isijinternational.ISIJINT-2017-593.
24. Chunyang Liu, Xu Gao, Shigeru Ueda, Muxing Guo, Shin-ya Kitamura. Composition Changes of Inclusions by Reaction with Slag and Refractory: A Review. ISIJ International. 2020. Vol. 60. Iss. 9. pp 1835-1848.
25. Wang H., Glaser B., Sichen D. Improvement of Resistance of MgO-Based Refractory to Slag Penetration by In Situ Spinel Formation. Metallurgical and Materials Transactions B. 2015. Vol. 46. pp. 749–757. DOI: 10.1007/s11663-014-0277-7.
26. Kazakov A. A., Murysev V. A., Rybalchenko I. V., Stepanov P. P. Non-metallic inclusions and quality of pipe joints obtained by high-frequency electric resistance welding. Chernye metally. 2022. No. 6. pp. 60-69.

Full content Non-metallic inclusions and hook cracks of high-frequency induction welded pipes